[China Aluminum Network] Because aluminum has a lighter material, aluminum ingots are widely used in construction, power, packaging, transportation, and consumer goods. Can be used to produce aluminum foil, aluminum alloy, anti-corrosion packaging materials can also be used for chemical industry aluminum alloy, utensils, cables, conductive body, the center alloy, decoration materials, daily necessities and so on.
In addition, aluminum ingots can also be used with other metals such as silicon, copper, magnesium, and iron to improve the distribution of pure aluminum in forgeability, chemical and physical defects.
For example: wrought aluminum-silicon (Al-Si) alloys. In the meantime, ZL101(A) alloys have been used to accept medium-duty cluttered parts such as aircraft parts, instruments, instrument housings, engine parts, car and boat parts, cylinder blocks, pump bodies, brake drums, and electrical parts.
Forged aluminum-zinc (Al-Zn) alloy. In the meantime, ZL401 alloy is mainly used as a forging part for various pressures, and the operating temperature does not exceed 200 degrees Celsius, and the structure of the car and the aircraft parts with a disorderly structure.
Forged aluminum-magnesium (Al-Mg) alloy. During this period, the ZL301 alloy is mainly used for medium-loaded parts with corrosive effects or in ice-cooled atmospheres and parts whose working temperature does not exceed 200 degrees Celsius, such as sea-wheel parts and machine housings.
The
Product introduction
HHCMS-240 type Carbon Molecular Sieve
HHCMS-240 is a new kind of non-polar adsorbent. It is designed to extract nitrogen-rich gas from the air. It is suitable for separating nitrogen from the air.
The most notable features of the carbon molecular sieve are high gas-producing efficiency and low waste, especially nitrogen with a purity higher than 99.9%.
It is widely used in large air separation and sheet making equipment, and the application field covers the high-end aspects such as the storage and transportation of crude oil in yibi ships.
Project parameters
The diameter of:1.0-1.3 1.3-1.5
Packing density:≥680-700kg/m³
The intensity of particle:≥95
Compressive strength abrasion:≤1%
The moisture content:≤0.5%
Standard packing:20Kg/barrel. 40Kg/barrel. 130Kg/barrel
The adsorption time of test condition was 58s with an average pressure of 1-2s
|
Adsorption pressure |
Nitrogen purity (%) |
Yield (Nm3/ h.t.) |
Nitrogen recovery rate |
|
0.8MPa |
99.99 |
95 |
24 |
|
99.9 |
160 |
29 |
|
|
99.5 |
240 |
35 |
|
|
99 |
320 |
42 |
|
|
98 |
400 |
43 |
|
|
97 |
490 |
48 |
|
|
96 |
560 |
51 |
|
|
95 |
620 |
55 |
|
|
0.6MPa |
99.99 |
75 |
27 |
|
99.9 |
130 |
30 |
|
|
99.5 |
190 |
37 |
|
|
99 |
260 |
42 |
|
|
98 |
320 |
44 |
|
|
97 |
390 |
50 |
|
|
96 |
445 |
52 |
|
|
95 |
500 |
56 |
Pay attention to
1. The nitrogen production equipment can reduce the adsorption temperature to better show its excellent nitrogen production performance under conditions;
2. Pay attention to low temperature drying and seal preservation during storage;
Molecular Sieves Hhcms-240,Molecular Sieves For Drying Solvents,Molecular Sieve Regeneration Process,Carbon Molecular Sieves Types
Zhejiang Changxing Haihua Chemical Co.,Ltd. , https://www.zjcxhhcms.com